1.4534 / PH 13-8 Mo
Standards
Mat. No.
1.4534
EU
X3CrNiMoAl13-8-2
AISI/ASTM
XM-13
UNS
S13800
Other
PH 13-8 Mo®
1.4534 is a stainless steel group that can be hardened by precipitation hardening.
315 °It exhibits high strength and stress corrosion resistance up to C.
Chemical Composition & Mechanical and Physical Properties
H 950
Tensile Strength MPa
1517
Yield Strength MPa
1413
Sertlik HRC
45
H 1000
Tensile Strength MPa
1413
Yield Strength MPa
1310
Sertlik HRC
43
H 1025
Tensile Strength MPa
1276
Yield Strength MPa
1207
Sertlik HRC
41
H1050
Tensile Strength MPa
1207
Yield Strength MPa
1138
Sertlik HRC
40
H1100
Tensile Strength MPa
1034
Yield Strength MPa
931
Sertlik HRC
34
H1150
Tensile Strength MPa
931
Yield Strength MPa
621
Sertlik HRC
30
Tavlama işlemi (Solution Heat Treated, Con.A) 9100-940 °It is made between C.
Application areas
In the Aviation Industry
In the Defense Industry
In applications requiring high corrosion resistance and strength, in valve components, nuclear reactor components, and jet engine parts.
Specifications
AMS 5629 Bars, Forgings, Rings and Extrusions,
AMS 5864 Plate,
ASTM A 564,
ASME SA564 Bars, Wires and Shapes,
ASTM A 693,
ASME SA693 Sheet, Plate and Strip,
ASTM A 705,
ASME SA705